Polycarbonate Solid Transparent Sheet
Our Polycarbonate Solid Transparent Sheet is a state-of-the-art material designed to provide exceptional clarity and strength.
Our Polycarbonate Solid Transparent Sheet is a state-of-the-art material designed to provide exceptional clarity and strength.
Our Polycarbonate Solid Translucent Sheet is an advanced material crafted to deliver outstanding durability and versatility.
Our Polycarbonate Solid Opaque Sheet is an innovative material engineered to offer superior strength and reliability.
S.No | Products Name | Colour | Thickness |
1 | PDM POLYCARBONATE SOLID TRANSPARENT SHEET | Clear, Bronze, Blue, Green, Solar Grey | 0.8mm to 15mm |
2 | PDM POLYCARBONATE SOLID TRANSLUCENT SHEET | Opal White, White Diffuser, Milky White | 0.8mm-15mm |
3 | PDM POLYCARBONATE SOLID OPAQUE SHEET | Milky White, Opal White, Black, Yellow, Dark Blue, Dark Grey, Dark Brown | 1.2mm - 15mm |
Property | Test Method | Testing Condition Width | Unit | Value |
Density | D-792 | g/cm3 | 1.2 | |
Heat Deflection Temperature | D-648 | Load: 1.82 MP | °C | 135 |
Short Time Service Temperature | °C | from -50 to +130 | ||
Long Time Service Temperature | °C | from -40 to +100 | ||
Coefficient of Linear Thermal Expansion | D-696 | mm/m °C | 0.065 | |
Thermal Conductivity | C-177 | W/m K | 0.21 | |
Tensile Strength at Yield | D-638 | 10 mm/min | Mpa or N/mm² | >65 |
Tensile Strength at Break | D-638 | 10 mm/min | Mpa or N/mm² | >60 |
Elongation at Yield | D-638 | 10 mm/min | % | 6 |
Elongation at Break | D-638 | % | >95 | |
Tensile Modulus of Elasticity | D-638 | 1 mm/min | MPa | 2350 |
Flexural Strength | D-790 | 1.3 mm/min. | MPa | 100 |
Flexural Modulus | D-790 | 1.3 mm/min. | MPa | 2600 |
Impact Falling Weight | ISO 6603/1 E50 | 3mm sheet | J | 158 |
Light Transmission | D-1003 | % | 82 – 92 | |
Haze | D-1003 | % | <0.5 | |
Flammability rate | UL 94 | V-2 or V-0 |